[1]冯筱倩,王 楠,张金铭,等. 高强度双组分聚氨酯防水涂料力学性能[J].湖北工业大学学报,2021,(5):70-72+90.
　FENG Xiaoqian,WANG Nan,ZHANG Jinming,et al. Research on Mechanical Property of High-Strength Two-Component Polyurethane Waterproof Coating[J].,2021,(5):70-72+90.
点击复制

 高强度双组分聚氨酯防水涂料力学性能()
分享到：

《湖北工业大学学报》[ISSN:1003-4684/CN:42-1752/Z]

卷:
期数:
2021年第5期
页码:
70-72+90
栏目:
湖北工业大学学报
出版日期:
2021-10-31

文章信息/Info

Title:
 Research on Mechanical Property of High-Strength Two-Component Polyurethane Waterproof Coating
文章编号:
1003-4684(2021)05-0070-03
作者:
 冯筱倩;  王 楠;  张金铭;  张高文
 湖北工业大学绿色轻工材料湖北省重点实验室， 湖北 武汉 430068
Author(s):
 FENG Xiaoqian;  WANG Nan;  ZHANG Jinming;  ZHANG Gaowen
 Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei Univ. of Tech., Wuhan 430068, China
关键词:
聚氨酯;  防水涂料;  双组分;  高强度
Keywords:
 ; polyurethane;  waterproof coating;  two-component;  high-strength
分类号:
TQ423.95
文献标志码:
A
摘要:
 采用两步预聚法，以二苯基甲烷二异氰酸酯（MDI）和聚醚多元醇为原料合成A组分预聚物，并与含少量聚醚多元醇和固化剂的B组分配合制备了一种环保型高强度双组分聚氨酯防水涂料。采用电子拉力机、扫描电子显微镜（SEM）对防水涂膜的力学性能及微观结构进行分析。结果表明，采用含更多苯环的异氰酸酯（MDI）为单体能得到强度更高的涂膜，且单体一次性单独加入时能进一步提高涂膜强度；随着A组分中R值的提高，拉伸强度呈递增趋势，但会导致断裂伸长率降低；采用非有机硅类消泡剂具有更好的消泡作用，有利于涂膜力学强度的提高。
Abstract:
 The two-step prepolymerization method is used to synthesize the A-component prepolymer with raw materials diphenylmethane diisocyanate (MDI) and polyether polyol. The A—component prepolymer is then prepared with B component containing a small amount of polyether polyol and curing agent to obtain the environmentally friendly high-strength two-component polyurethane waterproof coating. The mechanical properties and microstructure of the waterproof coating film were analyzed by electronic tensile machine and the scanning electron microscope (SEM). The results show that the use of isocyanate MDI with more benzene ring as the monomer can obtain a higher strength coating film. And when the monomer is added separately at one time, the strength of the coating film can be further improved. With the increase of the R value in the A component, the tensile strength tends to increase, whereas the elongation at break tends to decrease. The use of non-silicone defoamers has better defoaming effect and is beneficial to the improvement of the mechanical strength of the coating film.

参考文献/References:

[1] 林劲柏,庄希勇.我国聚氨酯的现状和发展[J].广东建材,2018,34(9):72-73.
[2] 李进卫.聚焦聚氨酯涂料及其市场观察与分析[J].染整技术,2015,37(10):9-15.
[3] 李超,刘兴邦,孙剑.新型聚氨酯防水涂料生产线及其工艺[J].中国建筑防水,2015(1):40-43.
[4] 余郑, 沈强, 洪晨雅，等. 高强度聚氨酯防水涂料的制备及其应用研究[J]. 聚氨酯工业2017, 32(3): 29-32.
[5] 焦明明，李红英，韩海军,等.环保型铁路用高强聚氨酯防水涂料的研制[J].新型建筑材料,2017,44(5):144-146.
[6] 国家标准化管理委员会. 聚氨酯防水涂料：GB/T 19250-2013[S]. 北京:中国标准出版社, 2013.
[7] 国家标准化管理委员会. 建筑防水涂料试验方法：GB/T 16777-2008[S]. 北京:中国标准出版社, 2008.
[8] 王敏, 郭睿, 张凯峰，等. 消泡剂的研究进展与发展趋势[J]. 商品混凝土, 2017（C1）: 55-57.

备注/Memo

备注/Memo:
 ［收稿日期］ 2020-12-28
［基金项目］ 国家自然科学基金（52073083）
［第一作者］ 冯筱倩(1996-)， 女，湖北黄石人， 湖北工业大学硕士研究生，研究方向为功能高分子合成与应用
［通信作者］ 张高文(1970-)， 男，湖北武汉人，工学博士，湖北工业大学教授，研究方向为功能高分子合成与应用
更新日期/Last Update: 2021-11-01