[1]周 翔,苏 骏,左国望.氯盐环境下混凝土氯离子传输和钢筋锈蚀研究[J].湖北工业大学学报,2020,(1):75-78.
　ZHOU Xiang,SU Jun,ZUO Guowang.Study on Chloride Ion Transport in Concrete and Steel Corrosion in Chloride Environment[J].,2020,(1):75-78.
点击复制

氯盐环境下混凝土氯离子传输和钢筋锈蚀研究()
分享到：

《湖北工业大学学报》[ISSN:1003-4684/CN:42-1752/Z]

卷:
期数:
2020年第1期
页码:
75-78
栏目:
湖北工业大学学报
出版日期:
2020-02-28

文章信息/Info

Title:
Study on Chloride Ion Transport in Concrete and Steel Corrosion in Chloride Environment
文章编号:
1003-4684(2020)01-0075-04
作者:
周 翔;  苏 骏;  左国望
湖北工业大学土木建筑与环境学院， 湖北 武汉 430068
Author(s):
ZHOU Xiang;  SU Jun;  ZUO Guowang
School of Civil Engin.,Architecture and Environment, Hubei Univ.of Tech.,Wuhan 430068,China
关键词:
干湿循环; 裂缝宽度; 钢筋锈蚀; 钢筋混凝土; 氯离子
Keywords:
dry-wet cycle;  crack width;  corrosion of reinforcement;  chloride ion
分类号:
TU528.1
文献标志码:
A
摘要:
通过对16组带裂缝100×100×400 mm的短梁进行在氯盐溶液的干湿循环试验，以裂缝宽度、混凝土保护层厚度和钢筋直径为变量，研究不同裂缝宽度的钢筋混凝土裂缝周围和沿裂缝深度的氯离子含量，以及裂缝底端钢筋锈蚀长度，探讨氯离子传输规律；钢筋锈蚀长度的影响因素；并提出钢筋锈蚀长度预测模型。结果表明：氯离子在带裂缝混凝土中以二维扩散的方式扩散，氯离子在裂缝周围40~60 mm区域的二维扩散效应表现得更加显著；混凝土深度为10 mm范围内氯离子浓度随裂缝增大的趋势相对平缓，当深度>10 mm后，其趋势变大；裂缝宽度对钢筋锈蚀长度影响最大，当裂缝宽度w＜0.3 mm时，钢筋锈蚀长度的预测值与试验值符合程度较好，钢筋锈蚀长度预测模型具有一定合理性。
Abstract:
Through the dry-wet cycle test of 16 groups of cracked 100×100×400 mm short beams in the chloride salt solution, the crack width, the thickness of the concrete protective layer and the diameter of the steel bar were used as variables to study the cracks around the reinforced concrete cracks with different crack widths. The chloride ion content along the depth of the crack and the length of the steel corrosion at the bottom of the crack were discussed. The chloride ion transport law and the influence factors of the corrosion length of the steel were discussed. The prediction model of the steel corrosion length was proposed. The results show that the chloride ion diffuses in the two-dimensional diffusion mode in the cracked concrete, and the two-dimensional diffusion effect of chloride ion in the 40~60 mm region around the crack is more significant. The chloride ion concentration increases with the crack in the concrete depth of 10mm. The trend is relatively flat. When the depth is greater than 10 mm, the trend becomes larger; the crack width has the greatest influence on the corrosion length of the steel. When the crack width is at w<0.3 mm, the predicted value of the corrosion length of the steel is in good agreement with the experimental value, and the steel corrosion is good. The length prediction model has certain rationality.

参考文献/References:

[1] 张红光，王曙光，刘伟庆.开裂开裂混凝土内氯离子扩散机理及数值模拟研究 [J ].混凝土，2014(9):19-25.
[2 ] Marsavina L, Audenaert K, De Schutter G,et al. Experimental and numerical determination of the chloride penetration in cracked concrete [J ]. Construction and Building Materials, 2009(23):264-274.
[3 ] Branko avija, Jos Pacheco, Erik Schlangen. Lattice modeling of chloride diffusion in sound and cracked concrete [J ].Cement&Concrete Composites, 2013(42):30-40.
[4 ] 金伟良，延永东，王海龙，等.饱和状态下开裂混凝土中氯离子扩散简化分析 [J ].交通科学与工程，2010，26（1）：23-28.
[5 ] 延永东，金伟良，王海龙，等.干湿交替作用下氯离子在开裂混凝土中的输运规律 [J ].中南大学学报，2013,44（5）：2060-2067.
[6 ] 陆春华，金伟良，延永东.氯盐干湿环境下受弯横向裂缝对钢筋混凝土耐久性影响 [J ].海洋工程, 2012, 30(1): 131-136, 144.
[7 ] 聂红宇，卫军.开裂状态对氯离子环境中混凝土结构耐久性影响研究 [D ].长沙：中南大学，2012.

备注/Memo

备注/Memo:
［收稿日期］ 2019-06-25
［第一作者］ 周   翔(1996-)，男，湖北武汉人，湖北工业大学硕士研究生，研究方向为工程结构抗震分析与加固技术
［通信作者］ 苏   骏(1971-)，男，安徽六安人，工学博士，湖北工业大学教授，研究方向为结构工程
更新日期/Last Update: 2020-04-11